Specification:
| Characteristics | Conditions | Specified Values | Units | ||
| Optical Characteristics: | |||||
| Attenuation | 1310nm | ≤0.34 | dB/km | ||
| 1383nm | ≤0.34 | dB/km | |||
| 1550nm | ≤0.20 | dB/km | |||
| 1625nm | ≤0.24 | dB/km | |||
| Attenuation vs. Wavelength
Max. a Difference |
1285~1330nm | ≤0.03 | dB/km | ||
| 1525~1575nm | ≤0.02 | dB/km | |||
| Dispersion Coefficient | 1285~1340nm | ≥-3.4 ≤3.4 | ps/nm·km | ||
| 1550nm | ≤18 | ps/nm·km | |||
| 1625nm | ≤22 | ps/nm·km | |||
| Zero Dispersion Wavelength | 1312±12 | nm | |||
| Zero Dispersion Slope | ≤0.091 | ps/nm2·km | |||
| Typical Value | 0.086 | ps/nm2·km | |||
| PMD | Maximum Individual Fibre | ≤0.2 | ps/ | ||
| Link Design Value (M=20, Q=0.01%) | ≤0.1 | ps/ | |||
| Typical Value | 0.04 | ps/ | |||
| Cable Cutoff Wavelength | ≤1260 | nm | |||
| Mode Field Diameter (MFD) | 1310nm | 8.8~9.6 | um | ||
| 1550nm | 9.9~10.9 | um | |||
| Effective Group Index of Refraction | 1310nm | 1.466 | |||
| 1550nm | 1.467 | ||||
| Point Discontinuities | 1310nm | ≤0.05 | dB | ||
| 1550nm | ≤0.05 | dB | |||
| Geometrical Characteristics: | |||||
| Cladding Diameter | 125.0±1.0 | um | |||
| Cladding Non-circularity | ≤1.0 | % | |||
| Coating Diameter | 245±7 | um | |||
| Coating-Cladding Concentricity Error | ≤12.0 | um | |||
| Coating Non-circularity | ≤6.0 | % | |||
| Core-cladding Concentricity Error | ≤0.6 | um | |||
| Curl (Radius) | ≥4 | m | |||
| Delivery Length | 2.1 to 50.4 | Km/reel | |||
| Enironmental Characteristics: (1310nm, 1550nm & 1625nm) | |||||
| Temperature Dependence Induced Attenuation at | -60°C to +85°C | ≤0.05 | dB/km | ||
| Temperatuere-humidity Cycling Induced Attenuation at | -10°C to +85°C, 98% RH | ≤0.05 | dB/km | ||
| Watersoak Dependence Induced Attenuation at | 23°C, for 30 days | ≤0.05 | dB/km | ||
| Damp Heat Dependence Induced Attenuation at | 85°C and 85% RH, for 30 days | ≤0.05 | dB/km | ||
| Dry Heat Aging at | 85°C | ≤0.05 | dB/km | ||
| Mechanical Specification: | |||||
| Proof Test | Off line | ≥9.0 | N | ||
| ≥1.0 | % | ||||
| ≥100 | kpsi | ||||
| Macro-bend Induced Attenuation | 1 turn around a mandrel of 32mm diameter | 1550nm | ≤0.05 | dB | |
| 100 turns around a mandrel of 50mm diameter | 1310nm & 1550nm | ≤0.05 | dB | ||
| 100 turns around a mandrel of 60mm diameter | 1625nm | ≤0.05 | dB | ||
| Coating Strip Force | Typical Average Force | 1.7 | N | ||
| Peak Force | ≥1.3 ≤8.9 | N | |||
| Dynamic Stress Corrosion Susceptibility Parameter | ≥20 | ||||